- Antistatic Floor Coatings
- Acid Alkali and Chemical Resistant Floor Coatings
- Sewage Resistant Floor Coatings
The electrical resistance is 106-109, applicable to the industry of aviation and computer, flammable and explosive workshops, and precise electronics instrument workshops.
2.Resistance to high pressure
3.Easy to clean
4.Great chemical resistance
5.Adjustable electrical resistance range
Typical flexible flooring system:
|
Features:
1.Stable and long term anti-static ability2.Resistance to high pressure
3.Easy to clean
4.Great chemical resistance
5.Adjustable electrical resistance range
Technical Data:
Item | Data | Test Condition |
Walkable time | about 24 hours (25°C) | |
Adhesion strength | ≥2.2MPa | GB5210, with concrete |
Anti-pressure strength | ≥90MPa | GB1041 |
Extension strength | ≥9.5MPa | GB13022 |
Resistance to impact | 50kg.cm | GB/T1732 Topcoat |
Surface hardness | ≥2H | Pencil hardness |
Gloss | ≥80% | 60°∠specular reflectance |
Resistivity | 105-108Ω | ASTM F150-98 |
Resistance to Chemicals (20°C, 1 month soak):
PH=1 H2SO4; HCI | No Change |
20% H2SO4; HCI | Slight discoloration or gloss loss |
10%HOCI | Slight discoloration or gloss loss |
5%NaOH | Slight discoloration or gloss loss |
CaOH2 | Slight discoloration or gloss loss |
5% ammonia | Slight discoloration or gloss loss |
BaCO3 | No Change |
CaCl2 | Slight discoloration or gloss loss |
CaCl2 | Slight discoloration or gloss loss |
Formaldehyde | Slight discoloration or gloss loss |
Mineral oil | No Change |
Super strong chemical resistance, could withstand long time soaking in strong acid and alkali, applicable to rigorous chemical corrosive areas, such as pickling workshops and acid - alkali industrial workshops.
2.Resistant to 75% concentration of sulfuric acid
3.Slip and abrasion resistance, high durability
4.Jointless construction, easy to clean
5.Easy to maintain
6.Resistance to the majority of acid, alkali and salt under 100°C
Typical flexible flooring system:
|
Features:
1.Super strong chemical resistance2.Resistant to 75% concentration of sulfuric acid
3.Slip and abrasion resistance, high durability
4.Jointless construction, easy to clean
5.Easy to maintain
6.Resistance to the majority of acid, alkali and salt under 100°C
Technical Data:
Item | Data | Test Condition |
Walkable time | about 24 hours (25°C) | |
Adhesion strength | ≥2.2MPa | GB5210,with concrete |
Anti-pressure strength | ≥130MPa | GB1041 |
Flexure strength | ≥100MPa | GB13022 |
Extension strength | ≥230MPa | GB177-92 |
Surface hardness | ≥2H | Pencil hardness |
Resistance to abrasion | ≤25mg | GB1769(750gf, 500N) |
Gloss | ≥80% | 60°∠specular reflectance |
Water absorption | ≤0.2% | |
Shrinkage | ≤0.2% |
Resistance to Chemicals:
75% H2SO4 | No Change (45℃) | Saturation ammonia | No Change (<100°C) |
70% H2SO4 | No Change (80℃) | 5% NaOH | No Change (<100℃) |
25% H2SO4 | No Change (<110℃) | 30% NaOH | No Change (room temperature) |
37% HCI | No Change (80℃) | 35% Na2CO3 | No Change (<80℃) |
40% HNO3 | No Change (room temperature) | Ammonia water, gas phase | No Change (room temperature) |
20% HNO3 | No Change (<60℃) | Xylene | No Change (<45℃) |
5% HNO3 | No Change (<80℃) | 90% Alcohol | No Change (room temperature) |
30% H2CrO4 | No Change (room temperature) | Glycol | No Change (<100℃) |
75% CH3COOH | No Change (<60℃) | Phenol | No Change (room temperature) |
25% CH3COOH | No Change (<100℃) | Urea | No Change (60℃) |
100% CH3COOH | No Change (room temperature) | Gasoline | No Change (80℃) |
20% HF | No Change (room temperature) | Flue gas | No Change (<200℃) |
10% HF | No Change (<60℃) | Zinc electrolyte | No Change (<60℃) |
30% H2O2 | No Change (<60℃) | Nickel electrolyte | No Change (<60℃) |
Suitable for dyeing plants, sewage tanks and drain ditches.
2.Resistance to permeation
3.Resistance to light and middle corrosive chemical soaking
Typical flexible flooring system:
|
Features:
1.Resistance to cracking2.Resistance to permeation
3.Resistance to light and middle corrosive chemical soaking
Technical Data:
Item | Data | Test Condition |
Walkable time | about 16 hours (25°C) | |
Adhesion strength | ≥2.2MPa | GB5210,with concrete |
Anti-pressure strength | ≥80MPa | GB1041 |
Extension strength | ≥200MPa | GB177-92 |
Flexure strength | ≥9.5MPa | GB13022 |
Surface hardness | ≥3H | Pencil hardness |
Resistance to abrasion | ≤20mg | GB1768(750gf, 500N) |
Resistance to Chemicals (20°C, 1 month soak):
PH=1 H2SO4; HCI | No Change |
20% H2SO4; HCI | Slight discoloration or gloss loss |
5% NaOH | No Change |
20% NaOH | Slight discoloration or gloss loss |
CaOH2 | Slight discoloration or gloss loss |
5% ammonia | Slight discoloration or gloss loss |
BaCO3 | No Change |
Na2CO3 | No Change |
CaCl2 | No Change |
Formaldehyde | Slight discoloration or gloss loss |
Mineral oil | No Change |
H2O2 | Slight discoloration or gloss loss |